A hydrogel scaffold of well-defined geometry was created and modified with laminin-derived peptides in an aqueous solution, thereby maintaining the geometry of the scaffold while introducing bioactive peptides that enhance cell adhesion and neurite outgrowth. By combining a fiber templating technique to create longitudinal channels with peptide modification, we were able to synthesize a scaffold that guided cell adhesion and neurite outgrowth of primary neurons. Scaffolds were designed to have numerous longitudinally oriented channels with an average channel diameter of 196±6μm to ultimately promote fasciculation of regenerating cables and a compressive modulus of 192±8kPa to match the modulus of the soft nerve tissue. Copolymerization of 2-hydroxylethyl methacrylate (HEMA) with 2-aminoethyl methacrylate (AEMA) scaffolds, provided primary amine groups to which two sulfhydryl terminated, laminin-derived oligopeptides, CDPGYIGSR and CQAASIKVAV, were covalently bound using the sulfo-(N-maleimidomethyl)cyclohexane-1-carboxylate (sulfo-SMCC) crosslinking agent. The concentration of peptides on the scaffolds was measured at 106±4μmol/cm² using the ninhydrin method and 92±9μmol/cm² using the BCA protein assay. The peptide modified P(HEMA-co-AEMA) scaffolds were easily fabricated in aqueous conditions, highly reproducible, well-defined, and enhanced neural cell adhesion and guided neurite outgrowth of primary chick dorsal root ganglia neurons relative to non-peptide-modified controls. The copolymerization of AEMA with HEMA can be extended to other radically polymerized monomers and is advantageous as it facilitates scaffold modification in aqueous solutions thereby obviating the use of organic solvents which can be cytotoxic and often disrupt scaffold geometry. The combination of well-defined chemical and physical stimuli described herein provides a means for guided regeneration both in vitro and in vivo.